Quick Details
Area of Origin: China (Mainland) Model Quantity:6571/6571 Polyester Film
Solution name: Polyester film Usage: for motor and transformer
Kind: Insulation Film Material: Polyester movie particle
Application: Large Temperature, Cable, motor and transformer and so forth. Melting level: ≥256
Usage: Insulation Protection,electrical cable and wire, For backing content of Flexbile laminate and Motor& Transformer,slot insulation, interphase insulation and liner insulation
Relative dielectric continuous (50Hz): 2.nine~three.4 Processing Sort: Numerous Extrusion
Tensile Strength: ≥120Mpa Width:325-3250mm or CZPT
Thickness: 12mic-500mic or CZPTers’ requirements Core Measurement:three”,six” or CZPTers’ demands
Roll Core ID:76mm(3″) or 152mm(six” ), Main materials: Paper or plastic
Feature: good dielectrical and large mechanical qualities, Heat-Resistant
Excess weight of roll: 100kg-200kg or CZPT Color: 6571 transparent, 6571milky white
Type: roll, tape, sheet, strips Thermal class: E(120ºC)
Guide time: 10-fifteen times for one particular container Certification: ROHS and CZPT
OEM, ODM services: Available Service: Die Slicing Slicing Slitting
Description
Polyester Film Composite Board is composed of layers polyester movie which is coated with high temperature adhesive. It has very good mechanical houses, electrical properties, shrinkage fee, drinking water absorption and reliable heat resistance. It is primarily utilised for the insulation amongst the high and low voltage coils of the dry kind transformer, which can be used as a substitute for the epoxy resin board and the phenolic resin board for the insulation tube and the finish insulation.
6571&6571 is a biaxial oriented polythylene terephthalate(PET)movie by means of melting, casting and stretching. This solution has great dielectric and large mechanical properties. It is broadly utilised for electrical insulation, such as slot insulation, interphase insulation and liner insulation in electric motors, and making insulating adaptable laminates.
Polyester Movie for CZPTal Insulation
6571-Polyester Film For CZPTal Insulation (Clear)
6571-Polyester Movie For CZPTal Insulation (Milky white)
6571/6571 Polyester movie is biaxially oriented polyethylene terephthalate (PET) film.
6571 is a transparent movie. 6571 is a milky white movie.
It is Course E insulating substance.
This merchandise has excellent dielectrical and large mechanical properties.
Thermal class: E(120ºC)
Characteristics: flat, minimal shrinkage, outstanding insulation homes, UL accepted
Apps
Polyester Film is created from Polyethylene terephthalate by casting & Biaxially oriented.
It is extensively utilised for the end wrap insulation, liner insulation of electrical oils, electromagnetic wire wrap insulation, cable wrapping on motor, transformer or other electrical appliances. It also be utilized for packaging, glass-metal, collar of outfits, etc.
It can be employed as an electrical insulation and as a laminate with other substrates.
In motor applications, picked kinds of polyester film can be utilized for ground insulation as slot liners and wedges, as nicely as stage insulation. In wire and cable applications, it is excellent for mechanical boundaries.
In addition, specialised polyester film can be employed in transformer and substantial-voltage distribution equipment to wrap the conductors. They are successful for use in hermetic applications with fridge and air conditioner motor / compressor assemblies.
Roll or tapes White Mylar pet movie,pet film tape, It is suitable for electrical insulation, these kinds of as slot insulation, Interphase insulation and liner insulation in electric motor, wrapping insulation for coils and cables, as nicely as generating insulating versatile composite material.
Advantages of PET
one. It has excellent mechanical houses and folding tolerance
2. It is resistant to oil, fat, dilute acid and alkali, most solvent.
three. It has outstanding temperature tolerance. Long-expression workable under 120°C ,
shortterm appliable underneath (150°Cor -70°C)slightly affection to its mechanical
qualities underneath substantial or low temperature
4. It has minimal gasoline and vapor permeability, and very good resistance to gasoline, h2o,
oil and odor.
5. It has large transparency and glossy, also can block ultraviolet ray.
6. It can be straight used in meals packing since it is non-poisonous, unscented with good sanitary protection.
6571 Transparent PET CZPTal Insulating Polyester Movie Feature:
Large transparency
Good brightness aluminum
Aluminum layer with very good adhesion
Great items approach capability
Outstanding mechanical qualities
Large transparency
CZPT color
Large impact
No crystal points or waves on surface
Great performance in folding
Secure good quality
Higher dimensional security
Easy coating residence
Exceptional electrical insulation.
6571 Milky White mylar polyester film
6571 polyester film is biaxially oriented polyethelene terphthalate(PET)film
6571 is a mily white film
this item has great dielectrical and higher mechanical properties.
Software:
It is suited for electrical insulation,these kinds of as slot insulation,interphase insulation and liner insulation in electrical motor transformer and other electrical appliances ,wrapping insulation for coils and cables,as effectively as making insulating adaptable composit material.
Purposes
• CZPTal versatile laminates CZPTal adaptable laminates (DMD, MMM and so forth)
• Wire & cable Insulation, slot liner insulation, interlayer insulation in Motor, transformer and so forth.
• Adhesive tapes
•. Polyester label.
•. Polyester tubing.
•. Keyboard insulation
• TV/Monitor insulation
Mylar polyester film for electric motor insulation biaxially oriented polyethelene terephthalate (PET) film, which is a milky white film. It is Course E insulating content. This solution has excellent dielectrical and substantial mechanical properties. It is appropriate for electrical insulation, this sort of as slot insulation, interphase insulation and liner insulation in electric motor, wrapping insulation for coils and cables, as properly as creating insulating adaptable composite content.
This kind of movie is utilised as an electrical insulation in motor applications, for ground insulation, as slot liner and wedges, phase insulation. it is best for mechanical obstacles, as nicely as in transformer and large-voltage distribution gear insulation separator and in addition its hardness is significantly suitable for automatic coil winding machines for enthusiast industries and is also employed in shirt collar bones for clothes industry.
6571 Characteristics
• Excellent electrical insulation.
• Thermal stability at elevated temperatures
• insulate course:E
• item description:
•Dimensional balance
• Coefficient of friction
•Tensile break power
•Tensile produce toughness
•Elongation at crack
•Chemical and electrical resistance
•High dielectric constant
•Lower extractable articles
•High electrical breakdown voltage
•High dimensional security
•Easy coating house
Standard property
3 layer co-extrusion construction
Higher tensile energy and lower heat shrinkage in higher operating temperature
Higher breakdown voltage and excellent electrical insulation
Steady good quality
CZPT parameter
| Homes | Unit NO. | one# | two# | 3# | 4# | five# | six# | seven# | eight# | Test strategy | ||
| Thickness | μm | 36 | 50 | seventy five | one hundred | 125 | one hundred fifty | 188 | 250 | GB12802.two | ||
| Tensile Energy | MD | Mpa | two hundred | 200 | 182 | 185 | one hundred seventy five | one hundred seventy | 172 | a hundred and eighty | GB12802.2 | |
| TD | Mpa | 210 | 198 | 198 | 190 | 186 | 206 | 185 | 200 | GB12802.2 | ||
| Elongation at split | MD | % | 115 | a hundred twenty five | a hundred and fifteen | 120 | one hundred fifty | 130 | 150 | 148 | GB12802.two | |
| TD | % | a hundred and five | 130 | one hundred ten | 102 | one hundred ten | 100 | 110 | 109 | GB12802.2 | ||
| Shrinkage | MD | % | 1.3 | one.four | one.three | 1.three | 1.4 | 1.4 | one.5 | 1.8 | GB12802.2 | |
| (150ºC30min) | TD | % | .8 | .8 | .nine | .8 | 1. | 1. | one. | one.five | GB12802.2 | |
| Breakdown voltage | V/μm | 220 | 188 | a hundred sixty five | one hundred forty five | 126 | 123 | 104 | ninety two | GB12802.two | ||
| Volume resistivity | Ω.m | 1.0×1014 | one.0×1014 | 1.0×1014 | one.0×1014 | one.0×1014 | 1.0×1014 | 1.0×1014 | one.0×1014 | GB12802.2 | ||
| Ralative dielectric continuous(48Hz-62Hz) | three. | 3. | 3. | three. | 3. | 3. | 3. | 3. | GB12802.two | |||
| Dielectric decline tangent(48Hz-62Hz) | two.8×10-3 | 2.8×10-3 | 2.8×10-three | 2.8×10-three | two.8×10-three | two.8×10-three | 2.8×10-3 | two.8×10-3 | GB12802.two | |||
| Haze | % | 10. | 14. | twenty. | 25. | 28. | 30. | 35. | 40. | GB2410 | ||
| Light Transmittance | % | 66 | sixty | 52 | 39 | 35 | 31 | 29 | 26 | GB2410 | ||
| Gloss(45)° | % | 98 | 90 | eighty four | eighty | seventy six | 76 | seventy four | 70 | GB8807 | ||
| Density | g/cm3 | 1.4 | 1.4 | one.4 | 1.4 | one.four | one.4 | 1.four | 1.four | GB12802.two | ||
| Flame retardancy | VTM-2 | VTM-two | VTM-2 | VTM-two | VTM-2 | VTM-2 | VTM-two | VTM-2 | ANSI/UL94
|
|||
| Properties | Models | Values | ||
| Tensile power(MD and TD) | 25μm~100μm >100μm~190μm >190μm |
mpa | ≥150 ≥140 ≥110 |
|
| Elongation at break (MD and TD) | 25μm~50μm >50μm~350μm |
% | ≥60 ≥80 |
|
| Shrinkage (MD and TD) | twenty five~190μm >190μm |
% | ≤3. ≤2. |
|
| Volume resistivity | Ω·M | ≥1.0×1014 | ||
| Relative dielectric constant (50Hz) | two.nine~3.four | |||
| Dielectric dissipation factor (50Hz) | ≤5.0×10-three | |||
| Density | kg/m3 | 6571 | 6571 | |
| 1390±10 | 1400+10-twenty | |||
| Melting level | ºC | ≥256 | ||
| Surface resistivity | Ω | ≥1.0×1013 | ||
| Electrolytic corrosion | Ocular estimate | Course | A1 | |
| Metallic conductivity tensile Toughness approach | % | ≤2 | ||
| Dimensional steadiness in substantial temp. |
With pressure | ºC | ≥200 | |
| With force | ≥200 | |||
CZPT indicators (aluminum substrate physical, mechanical performance):
| Functionality | Device | Take a look at technique | Focus on | |
| Tensile toughness | TD≥ | MPa | ASTM D-882 | 230 |
| MD≥ | MPa | 230 | ||
| Elongation at break | MD≥ | % | ASTM D-882 | one hundred twenty |
| TD≥ | % | one hundred twenty | ||
| Modulus of elasticity | MD≥ | MPa | ASTM D-882 | 4300 |
| TD≥ | MPa | 4500 | ||
| Heat shrinkage rate | MD≤ | % | ASTM D-1204 | 2 |
| 150ºC,30min | TD≤ | % | .five | |
| Coefficient of friction | Static≤ | ASTM D-1894 | .55 | |
| Dynamic≤ | .45 | |||
| Haze | CZPT type≤ | % | ASTM D-1003 | two |
| Highlight type≤ | % | 1.6 | ||
| Glossiness | CZPT type≥ | % | GB/T 8807 | 120 |
| Highlight type≥ | % | a hundred thirty | ||
| Surface pressure | No treated≤ | Dyne/cm | ASTM D-2578 | forty two |
| Treated≥ | Dyne/cm | fifty two | ||
Note: unique items can be CZPT according to customer particular specifications.
Principal Specification
| Houses | Thickness | Device | Price |
| Thickness Tolerance |
twelve~one hundred mm ≥100 mm |
% | ≤±5 ≤±4 |
| Tensile energy | twelve~≤100 mm >100~188 mm ≥188 mm |
MPa | ≥150 ≥140 ≥110 |
| Elongation at rupture | twelve~23mm twenty five~<50 mm ≥50~350 mm |
% | ≥40 ≥60 ≥80 |
| Heat Shrinkage |
12~23mm twenty five~188 mm ≥188 mm |
% | ≤3.five ≤3. ≤2. |
| Breakdown strength | 12mm 19mm 23mm twenty five mm 36 mm fifty mm 75 mm one hundred mm 125 mm one hundred fifty mm 188 mm 250 mm three hundred mm 350mm |
V / mm | ≥208 ≥190 ≥174 ≥170 ≥150 ≥130 ≥105 ≥ 90 ≥ 75 ≥ 70 ≥ sixty five ≥ 60 ≥ 55 ≥ 50 |
Note: Earlier mentioned values are the accumulative normal kinds by recognized tests method, but, in buy to make sure you to pick our goods properly, you should refer to over specification and take a look at the samples primarily based on your using goal or feel free to speak to us for much more details.
FAQ
Q1: How about MOQ?
MOQ is according to diverse items. What ever you need to have, we are glad to quote very best value with excellent quality.
Q2: Can you send samples for testing?
500g Samples are cost-free provided, but categorical freight need to be taken by client. Soon after generating order, we would like to return freight back.
Q3: How can you assure the good quality of mass merchandise is identical as the sample despatched to me ahead of?
We stored yet another identical sample and marked on company when we despatched to buyer. So our generation will be primarily based on.
This autumn: Which bundle do you use?
Package deal is essential element to keep away from goods breaking in transportation. We will choose appropriate packing count on materials.
Q5: When customer reply top quality troubles soon after decide up products, how to deal with?
1) CZPTer could source images of issued products for our income workers and then we will validate which element is wrong.
two) If the issue is verified, company will negotiate with consumers and compensate in coming orders.
Q6:What are your main goods?
A:For oil immersed transformers, like Diamond dotted paper/DDP, Crepe paper tube, pressboard and so on.
For dry kind transformers, like Class F DMD,NMN,AMA,NHN, and so on.
Packaging & Delivery
Packaging Details: each roll with protecting film and carton, then with regular export pallets
Roll Core ID:76mm(3″) or 152mm(6″ ), Main materials: Paper or plastic
Shipping and delivery Element: 10-fifteen times for a container
Port: ZheJiang , HangCZPT, HangCZPT
Direct Time : Shipped in fifteen days soon after payment
Please Contact Us
Miss: lydia